Oxydehydrogenation of isobutyric acid and its lower alkyl esters

ABSTRACT

Isobutyric acid or a lower alkyl ester thereof is oxidatively dehydrogenated in the vapor phase to produce the corresponding α,B-olefinically unsaturated derivative by contact with a heterogeneous catalyst in the presence of molecular oxygen. The catalyst is composed of the calcined phosphates of chromium, molybdenum and tungsten.

BACKGROUND OF THE INVENTION

1. Field of the Invention

This invention relates to the conversion of isobutyric acid or its equivalents and lower alkyl esters thereof correspondingly to methacrylic acid or its equivalents and lower alkyl esters thereof.

2. Description of the Prior Art

There exists considerable prior art relating to the oxydehydrogenation of the lower saturated aliphatic monocarboxylic acids to produce the corresponding α,B-olefinically unsaturated acids. Early work in this area involved thermal, vapor phase oxydehydrogenation of the saturated aliphatic carboxylic acid in the presence of oxygen and iodine. This approach has not been particularly successful from a commercial standpoint. This is understandably so inasmuch as iodine is costly, exhibits extreme corrosivity properties and poses considerable problems in realizing complete recovery of the comparatively large amount thereof required in the process. The heterogeneous catalytic method for oxydehydrogenation according to the prior art appears to be the more attractive route to the commercial production of olefinically unsaturated monocarboxylic acids. The prior art heterogeneous oxydehydrogenation catalysts useful for this purpose include some heteropoly acids, such as phosphomolybdic acid, optionally with tungsten and/or vanadium. Another type of catalyst included in the prior art is iron phosphate.

Iron phosphate subjected to calcination exists in several crystalline phases or species. It is not known at this time which species is or are catalytically active. There is evidence that the presence of certain extrinsic metal components in the catalyst preparation serves to facilitate the formation of active catalyst. For instance, U.S. Pat. No. 3,948,959 discloses that an alkali or alkaline earth metal can be the extrinsic metal component for this purpose.

SUMMARY OF THE INVENTION

In accordance with this invention, a catalytic process is provided for the oxidative dehydrogenation of a saturated aliphatic monocarboxylic acid or lower alkyl ester thereof, such as isobutyric acid or methyl isobutyrate, to the corresponding α,B-olefinically unsaturated derivative thereof, such as methacrylic acid or methyl methacrylate. The process of this invention comprises contacting a heterogeneous catalyst at a temperature in the range of from 300°-500° C. with a mixture of the saturated aliphatic monocarboxylic acid and molecular oxygen, said catalyst being a calcined material compound of the combined oxides of chromium, molybdenum, tungsten and phosphorous. Although the exact nature and fine structure of this catalyst is not known at the present time, it can be conveniently further defined as conforming to the gram-atom empirical formula Cr_(a) P_(b) W_(c) Mo_(d) O_(x) wherein a is 0.01-1.0, b is 0.05-3.0, c is 0.01-3.0, d is 1-12.0 and x represents the number of oxygen atoms required to satisfy the uncombined positive valences of the other elements shown in the formula.

DESCRIPTION OF THE PREFERRED EMBODIMENT

There are a number of techniques which can be used for preparing the catalyst useful in the process of this invention. Of these, the more facile methods involve preparing the integral catalyst composition prior to calcination. This can be readily accomplished by the so-called slurry method or the precipitation method. In the latter method an aqueous solution of salts of the various elements and phosphoric acid is first prepared and is then neutralized with an appropriate base so as to precipitate the mixed metal oxides. The precipitate is washed and dried prior to calcination. In the alternative, one can add ammonium phosphate to a solution of the metal salts causing direct precipitation of the mixed metal oxides. As indicated, any water-soluble salt of chromium, tungsten, and molybdenum can be used in the preparation of the solution. The nitrate salts are suitable water-soluble salts for this purpose and are readily available and have desirable solubility characteristics.

The so-called slurry method is the preferred catalyst preparation method because of its convenience. In accordance with this procedure, the aqueous solution of the metal salts together with the phosphoric acid is obtained as previously noted. The solution is then heated with stirring to remove water and this is continued until the mass is so thick that it cannot be stirred. The resulting residue is then broken up and heated to a moderately higher temperature in the order of about 120° C. until the mass is completely dried. The resulting solid may be sized and calcined. Suitable calcination temperatures range from 250°-550° C. Applicable periods of calcination range from 2-30 hours.

The use of a support or carrier for the catalyst is included in either of the catalyst preparative methods mentioned above. For instance, in the slurry method colloidal silica or any other form of silica as well as other support material such as alumina, pumice, quartz, zirconia, titanium dioxide, carbon, silicon carbide, etc. can be included prior to the water removal step. Similarly, the precipitation of the metal phosphates can be accomplished in the presence of suspended particles of the support material in the alternate method described above.

The process of this invention can be carried out using the catalyst in the form of a fluid bed reactor, a stirred tank reactor or in a fixed bed or packed bed reactor or any combination of these types of reactors. Because of the convenience associated with the use of a fixed bed reactor in a small scale operation, such a reactor will be exemplified herein. In the preferred mode of operation the feed to the reactor comprises a pre-heat temperature. A pre-heat temperature in the range of about 300° to 500° C. is customarily used. The oxydehydrogenation reaction can be carried out in the range of from 300° to 500° C. More generally a temperature of from 275° to 425° C. provides for optimum processing.

The mole ratio of molecular oxygen to carboxylic acid is from 0.5 to 1.5 and more preferably from 0.7 to 0.75 in the case where the carboxylic acid is isobutyric acid, per se. Although steam is not necessary for the reaction, its presence is desirable in the feed because it is believed to act beneficially as a heat sink and in minimizing combustion of the carboxylic acid to undesirable waste products. The mole ratio of water to the carboxylic acid in the feed should be from about 0.5 to 20. The optimum ratio is from 1.2 to 5.0.

Another important parameter is the concentration of the organic reactant in the feed. The organic reactant carboxylic acid or ester should be present in the feed in from 0.1 to 20 mole percent. From the standpoint of achieving a reasonable through-put combined with an acceptable yield, the concentration of the reactant in the feed is from about 3-6 mole percent. Concentration of reactant in the feed is controlled to a large degree by the amount of inert gas present. The preferred inert gas or diluent is nitrogen although other inert gases such as carbon dioxide, helium, argon, and the like are suitable. Air is a very convenient source of oxygen plus inert diluent.

Another important parameter is contact time in the process of this invention. Contact or reaction time is defined for the purpose of this invention as the catalyst volume divided by the volume of gas feed per second at the reaction temperature. The catalyst volume is the bulk volume occupied by the catalyst in the reactor. The term catalyst in this sense not only includes the elements shown in the above empirical formula but is meant to include also any support material which may be present. Accordingly, reaction times can range from 0.05 to 3.0 seconds and preferably in the order of from 0.1 to 1.0 second. The reaction is preferably carried out at or near atmospheric pressure although the use of higher pressures up to about 10 atmospheres is contemplated.

The process of this invention is further illustrated in the following specific examples.

EXAMPLE I

A slurry was made using 60.0 grams of chromium nitrate, 25.0 grams of tungstic acid, 190.0 grams of ammonium heptamolybdate and 150.0 ml. of concentrated phosphoric acid in 500.0 ml. distilled water. The slurry is then mixed with 100.0 ml. of Ludox 40 HS containing 40.0% by wt. silica in water. The slurry is dried at 120° C. for 15 hours and calcined in air at 350° C. for 15 hours.

The final catalyst composition was found by analysis to have the following composition:

    Cr.sub.0.3 P.sub.1.8 W.sub.0.02 Mo.sub.1.2 O.sub.x /SiO.sub.2 15%

Where x is the number of oxygen atoms required to satisfy the sum of the unshared positive valences of the other elements present in the catalyst.

EXAMPLE II

This example illustrates the use of the catalyst described in Example I in the oxydehydrogenation of isobutyric acid to produce methacrylic acid. The procedure consisted of feeding a pre-heated mixture of isobutyric acid, oxygen, nitrogen and steam through a stainless steel tube of 1/2" O.D. (3/8" I.D.) and approximately 18" in length containing the catalyst as a 15 cc. packed bed maintained at the reaction temperature.

The pre-heater consisted of a length of stainless steel tubing similar to the reactor but packed with glass beads. Any carbon dioxide formed in the course of the reaction was absorbed in an Ascarite tube protected by a calcium sulfate absorber for any uncondensed water. The condensed organic product was separated from the water, collected and analyzed by the internal standard method of gas chromatography.

Selectivity to methacrylic acid represents the mole ratio of methacrylic acid found in the reaction effluent to that of the isobutyric acid consumed in the reaction.

The feed to the reactor consisted of isobutyric acid:oxygen:water:nitrogen in the corresponding mole ratio of 5.0:3.5:2.5:89.0. The reaction temperature was 518° F. and the contact time was 0.5 sec. Several runs were made with the results shown in the following table. The mole ratio of H₂ O/isobutyric acid was 2.60.

                  TABLE                                                            ______________________________________                                         Mole % Isobutyric                                                                           % Conversion of                                                                             % Selectivity to                                     Acid in Feed Isobutyric Acid                                                                             Methacrylic Acid                                     ______________________________________                                         4.41         86.7         66.9                                                 5.93         94.6         59.2                                                 5.98         90.4         59.4                                                 5.02         87.0         65.5                                                 4.28         86.6         67.4                                                 4.23         85.3         66.2                                                 4.32         77.6         70.8                                                 ______________________________________                                     

I claim:
 1. In a process for the catalytic conversion of isobutyric acid or a lower alkyl ester thereof to the corresponding α,B-olefinically unsaturated derivative by oxydehydrogenation wherein a catalyst is contacted with a gaseous feed stream containing said acid or ester and molecular oxygen at a temperature between 300° and 550° C.; the improvement comprising using as catalyst a material having the gram-atom empirical formula Cr_(a) P_(b) W_(c) Mo_(d) O_(x) wherein a is 0.01 to 1.0, b is 0.05 to 3.0, c is 0.01 to 3.0, d is 1 to 12.0, and x is determined by satisfying the sum of the unshared positive valences of the other elements shown in the formula.
 2. The process of claim 1 wherein isobutyric acid is converted to methacrylic acid.
 3. The process of claim 2 wherein the catalyst has the gram-atom empirical formula Cr₀.3 P₁.8 W₀.02 Mo₁.2 O_(x). 